SLO3-100 Ozone Aging Chamber

Overview.

Ozone content in the atmosphere is very small but the main factor of rubber cracking, SLO3-100 ozone aging chamber is to simulate and strengthen the atmospheric ozone environment, study the role of ozone on the rubber law, rapid identification and evaluation of rubber anti-ozone aging performance and anti-ozone agent protection effectiveness of the method, and then take effective anti-aging measures to improve the service life of rubber products. This equipment is suitable for non-metallic materials, organic materials (paint, rubber, plastic, paint, pigment, etc.) in the ozone conditions of the aging test.

Technical Parameters.

Studio Size

 400×450×550mm(D×W×H)
temperature range

25℃ -65℃ Adjustable

volatility

 ≤±0.5°C
evenness

≤2°C

Humidity range

 30-65%RH
Humidity uniformity

+2, -3% RH

heating rate

 0.7～1.0℃/min
ozone concentration

50-500pphm adjustable

Ozone concentration deviation

 10% National Standard
gas velocity

8～16mm/s

Rotary speed of specimen holder

 0 to 50mm/s
Test gas flow rate

0-60L/min

Rotation speed of the sample frame

 1 rpm (adjustable)
Fixture elongation

5 to 45%

total power

5.5KW
New specimen holder Each fixture can be installed test piece stretching to meet the type Ⅰ dumbbell piece and the actual workpiece.

Dynamic and static tensile frame